C70260 Copper vs. R05240 Alloy

C70260 copper belongs to the copper alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C70260 copper and the bottom bar is R05240 alloy.

UNS C70260 (CW111C) Nickel-Silicon Copper UNS R05240 Tantalum-Niobium Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		150

Elongation at Break, %		9.5 to 19
Elongation at Break, %		25

Poisson's Ratio		0.34
Poisson's Ratio		0.36

Shear Modulus, GPa		44
Shear Modulus, GPa		57

Tensile Strength: Ultimate (UTS), MPa		520 to 760
Tensile Strength: Ultimate (UTS), MPa		270

Tensile Strength: Yield (Proof), MPa		410 to 650
Tensile Strength: Yield (Proof), MPa		170

Thermal Properties

Latent Heat of Fusion, J/g		220
Latent Heat of Fusion, J/g		210

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		190

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		6.8

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		14

Embodied Water, L/kg		310
Embodied Water, L/kg		460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		46 to 140
Resilience: Ultimate (Unit Rupture Work), MJ/m³		59

Resilience: Unit (Modulus of Resilience), kJ/m³		710 to 1810
Resilience: Unit (Modulus of Resilience), kJ/m³		90

Stiffness to Weight: Axial, points		7.3
Stiffness to Weight: Axial, points		6.3

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		13

Strength to Weight: Axial, points		16 to 24
Strength to Weight: Axial, points		5.4

Strength to Weight: Bending, points		16 to 21
Strength to Weight: Bending, points		6.8

Thermal Shock Resistance, points		18 to 27
Thermal Shock Resistance, points		18

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.010

Copper (Cu), %		95.8 to 98.8
Copper (Cu), %		0

Hydrogen (H), %		0
Hydrogen (H), %		0 to 0.0015

Iron (Fe), %		0
Iron (Fe), %		0 to 0.010

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.020

Nickel (Ni), %		1.0 to 3.0
Nickel (Ni), %		0 to 0.010

Niobium (Nb), %		0
Niobium (Nb), %		35 to 42

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.010

Oxygen (O), %		0
Oxygen (O), %		0 to 0.020

Phosphorus (P), %		0 to 0.010
Phosphorus (P), %		0

Silicon (Si), %		0.2 to 0.7
Silicon (Si), %		0 to 0.0050

Tantalum (Ta), %		0
Tantalum (Ta), %		57.9 to 65

Titanium (Ti), %		0
Titanium (Ti), %		0 to 0.010

Tungsten (W), %		0
Tungsten (W), %		0 to 0.050

Residuals, %		0 to 0.5
Residuals, %		0