C70600 Copper-nickel vs. ASTM B685 Alloy

C70600 copper-nickel belongs to the copper alloys classification, while ASTM B685 alloy belongs to the otherwise unclassified metals. They have 40% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is C70600 copper-nickel and the bottom bar is ASTM B685 alloy.

UNS C70600 (CW352H) Copper-Nickel ASTM B685 Palladium-Copper Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.34
Poisson's Ratio		0.37

Shear Modulus, GPa		46
Shear Modulus, GPa		43

Tensile Strength: Ultimate (UTS), MPa		290 to 570
Tensile Strength: Ultimate (UTS), MPa		660 to 1060

Thermal Properties

Latent Heat of Fusion, J/g		220
Latent Heat of Fusion, J/g		180

Melting Completion (Liquidus), °C		1150
Melting Completion (Liquidus), °C		1230

Melting Onset (Solidus), °C		1100
Melting Onset (Solidus), °C		1200

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		300

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		9.8
Electrical Conductivity: Equal Volume, % IACS		5.0

Electrical Conductivity: Equal Weight (Specific), % IACS		9.9
Electrical Conductivity: Equal Weight (Specific), % IACS		4.1

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		11

Common Calculations

Stiffness to Weight: Axial, points		7.7
Stiffness to Weight: Axial, points		6.1

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		15

Strength to Weight: Axial, points		9.1 to 18
Strength to Weight: Axial, points		17 to 27

Strength to Weight: Bending, points		11 to 17
Strength to Weight: Bending, points		16 to 21

Thermal Shock Resistance, points		9.8 to 19
Thermal Shock Resistance, points		28 to 46

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		84.7 to 90
Copper (Cu), %		39.5 to 40.5

Iron (Fe), %		1.0 to 1.8
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0 to 0.050
Lead (Pb), %		0 to 0.030

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0

Nickel (Ni), %		9.0 to 11
Nickel (Ni), %		0

Palladium (Pd), %		0
Palladium (Pd), %		59 to 60.5

Silver (Ag), %		0
Silver (Ag), %		0 to 0.1

Zinc (Zn), %		0 to 1.0
Zinc (Zn), %		0 to 0.060

Residuals, %		0
Residuals, %		0 to 0.2