C70600 Copper-nickel vs. N07041 Nickel
C70600 copper-nickel belongs to the copper alloys classification, while N07041 nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C70600 copper-nickel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 220 |
| Elongation at Break, % | 3.0 to 34 | |
| 14 |
| Shear Strength, MPa | 190 to 330 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 570 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 63 to 270 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1100 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 44 | |
| 11 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.5 to 160 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 16 to 290 | |
| 2510 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 9.1 to 18 | |
| 47 |
| Strength to Weight: Bending, points | 11 to 17 | |
| 34 |
| Thermal Diffusivity, mm2/s | 13 | |
| 3.0 |
| Thermal Shock Resistance, points | 9.8 to 19 | |
| 38 |