C70620 Copper-nickel vs. C77400 Nickel Silver
Both C70620 copper-nickel and C77400 nickel silver are copper alloys. They have 56% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C70620 copper-nickel and the bottom bar is C77400 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Rockwell B Hardness | 65 to 87 | |
| 73 |
| Shear Modulus, GPa | 46 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 570 | |
| 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 130 |
| Melting Completion (Liquidus), °C | 1120 | |
| 810 |
| Melting Onset (Solidus), °C | 1060 | |
| 770 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 25 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.5 |
| Embodied Energy, MJ/kg | 51 | |
| 57 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 9.3 to 18 | |
| 20 |
| Strength to Weight: Bending, points | 11 to 17 | |
| 19 |
| Thermal Shock Resistance, points | 10 to 20 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 86.5 to 90 | |
| 43 to 47 |
| Iron (Fe), % | 1.0 to 1.8 | |
| 0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 9.0 to 11 | |
| 9.0 to 11 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 41.3 to 48 |
| Residuals, % | 0 | |
| 0 to 0.5 |