C70700 Copper-nickel vs. ASTM B617 Coin Silver

C70700 copper-nickel belongs to the copper alloys classification, while ASTM B617 coin silver belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C70700 copper-nickel and the bottom bar is ASTM B617 coin silver.

UNS C70700 (CuNi10) Copper-Nickel ASTM B617 Coin Silver Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		75

Elongation at Break, %		39
Elongation at Break, %		1.1 to 22

Poisson's Ratio		0.34
Poisson's Ratio		0.37

Shear Modulus, GPa		46
Shear Modulus, GPa		28

Shear Strength, MPa		220
Shear Strength, MPa		180 to 290

Tensile Strength: Ultimate (UTS), MPa		320
Tensile Strength: Ultimate (UTS), MPa		290 to 520

Thermal Properties

Latent Heat of Fusion, J/g		220
Latent Heat of Fusion, J/g		120

Melting Completion (Liquidus), °C		1120
Melting Completion (Liquidus), °C		870

Melting Onset (Solidus), °C		1060
Melting Onset (Solidus), °C		780

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		250

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		11
Electrical Conductivity: Equal Volume, % IACS		83

Electrical Conductivity: Equal Weight (Specific), % IACS		12
Electrical Conductivity: Equal Weight (Specific), % IACS		72

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		10

Common Calculations

Stiffness to Weight: Axial, points		7.6
Stiffness to Weight: Axial, points		4.1

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		10
Strength to Weight: Axial, points		7.7 to 14

Strength to Weight: Bending, points		12
Strength to Weight: Bending, points		9.3 to 14

Thermal Shock Resistance, points		12
Thermal Shock Resistance, points		14 to 25

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		88.5 to 90.5
Copper (Cu), %		9.0 to 10.4

Iron (Fe), %		0 to 0.050
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0
Lead (Pb), %		0 to 0.030

Manganese (Mn), %		0 to 0.5
Manganese (Mn), %		0

Nickel (Ni), %		9.5 to 10.5
Nickel (Ni), %		0 to 0.010

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silver (Ag), %		0
Silver (Ag), %		89.6 to 91

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.060

Residuals, %		0
Residuals, %		0 to 0.060