C70700 Copper-nickel vs. EN 1.6220 Steel

C70700 copper-nickel belongs to the copper alloys classification, while EN 1.6220 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C70700 copper-nickel and the bottom bar is EN 1.6220 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 73
170
Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 39
23 to 25
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 46
73
Tensile Strength: Ultimate (UTS), MPa 320
550 to 580
Tensile Strength: Yield (Proof), MPa 110
340

Thermal Properties

Latent Heat of Fusion, J/g 220
250
Maximum Temperature: Mechanical, °C 220
400
Melting Completion (Liquidus), °C 1120
1460
Melting Onset (Solidus), °C 1060
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 59
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 34
2.1
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.5
Embodied Energy, MJ/kg 52
19
Embodied Water, L/kg 300
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 51
300 to 310
Stiffness to Weight: Axial, points 7.6
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 10
19 to 20
Strength to Weight: Bending, points 12
19 to 20
Thermal Diffusivity, mm2/s 17
14
Thermal Shock Resistance, points 12
16 to 17

Alloy Composition

Carbon (C), % 0
0.17 to 0.23
Copper (Cu), % 88.5 to 90.5
0
Iron (Fe), % 0 to 0.050
96.7 to 98.8
Manganese (Mn), % 0 to 0.5
1.0 to 1.6
Nickel (Ni), % 9.5 to 10.5
0 to 0.8
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0
0 to 0.030
Residuals, % 0 to 0.5
0