C71000 Copper-nickel vs. S35315 Stainless Steel
C71000 copper-nickel belongs to the copper alloys classification, while S35315 stainless steel belongs to the iron alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C71000 copper-nickel and the bottom bar is S35315 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 200 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Rockwell B Hardness | 59 to 85 | |
| 82 |
| Shear Modulus, GPa | 49 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 560 | |
| 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 240 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1200 | |
| 1370 |
| Melting Onset (Solidus), °C | 1150 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 480 |
| Thermal Conductivity, W/m-K | 43 | |
| 12 |
| Thermal Expansion, µm/m-K | 15 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.5 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.6 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 34 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.3 | |
| 5.7 |
| Embodied Energy, MJ/kg | 63 | |
| 81 |
| Embodied Water, L/kg | 290 | |
| 220 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 10 to 18 | |
| 26 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 23 |
| Thermal Diffusivity, mm2/s | 12 | |
| 3.1 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.040 to 0.080 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.1 |
| Chromium (Cr), % | 0 | |
| 24 to 26 |
| Copper (Cu), % | 73.5 to 80.5 | |
| 0 |
| Iron (Fe), % | 0.5 to 1.0 | |
| 33.6 to 40.6 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 19 to 23 | |
| 34 to 36 |
| Nitrogen (N), % | 0 | |
| 0.12 to 0.18 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 1.2 to 2.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |