C71500 Copper-nickel vs. Nuclear Grade Hafnium
C71500 copper-nickel belongs to the copper alloys classification, while nuclear grade hafnium belongs to the otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is C71500 copper-nickel and the bottom bar is nuclear grade hafnium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 78 |
| Poisson's Ratio | 0.33 | |
| 0.26 |
| Shear Modulus, GPa | 52 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 620 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 130 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 140 |
| Thermal Expansion, µm/m-K | 16 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 13 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.6 | |
| 3.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 11 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 7.4 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 8.4 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 55 |
Alloy Composition
| Copper (Cu), % | 63.5 to 70.6 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 99.8 to 100 |
| Iron (Fe), % | 0.4 to 1.0 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 29 to 33 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.23 |