C72200 Copper-nickel vs. C27400 Brass
Both C72200 copper-nickel and C27400 brass are copper alloys. They have 63% of their average alloy composition in common.
For each property being compared, the top bar is C72200 copper-nickel and the bottom bar is C27400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 110 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Rockwell B Hardness | 71 to 86 | |
| 53 to 91 |
| Rockwell Superficial 30T Hardness | 64 to 75 | |
| 52 to 78 |
| Shear Modulus, GPa | 48 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 580 | |
| 370 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 120 |
| Melting Completion (Liquidus), °C | 1180 | |
| 920 |
| Melting Onset (Solidus), °C | 1120 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 34 | |
| 120 |
| Thermal Expansion, µm/m-K | 16 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.5 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.6 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 23 |
| Density, g/cm3 | 8.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 2.7 |
| Embodied Energy, MJ/kg | 59 | |
| 45 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 13 to 23 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 14 to 21 |
| Thermal Diffusivity, mm2/s | 9.6 | |
| 37 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 12 to 22 |
Alloy Composition
| Chromium (Cr), % | 0.3 to 0.7 | |
| 0 |
| Copper (Cu), % | 78.1 to 84.2 | |
| 61 to 64 |
| Iron (Fe), % | 0.5 to 1.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 15 to 18 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 35.6 to 39 |
| Residuals, % | 0 | |
| 0 to 0.3 |