C72200 Copper-nickel vs. N10629 Nickel
C72200 copper-nickel belongs to the copper alloys classification, while N10629 nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C72200 copper-nickel and the bottom bar is N10629 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 220 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Rockwell B Hardness | 71 to 86 | |
| 88 |
| Shear Modulus, GPa | 48 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 580 | |
| 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 910 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1610 |
| Melting Onset (Solidus), °C | 1120 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Expansion, µm/m-K | 16 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 75 |
| Density, g/cm3 | 8.9 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 15 |
| Embodied Energy, MJ/kg | 59 | |
| 190 |
| Embodied Water, L/kg | 300 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 22 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 26 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 22 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.1 to 0.5 |
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0.3 to 0.7 | |
| 0.5 to 1.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 78.1 to 84.2 | |
| 0 to 0.5 |
| Iron (Fe), % | 0.5 to 1.0 | |
| 1.0 to 6.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 26 to 30 |
| Nickel (Ni), % | 15 to 18 | |
| 65 to 72.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |