C72700 Copper-nickel vs. ASTM B563 Pd-Ag-Cu
C72700 copper-nickel belongs to the copper alloys classification, while ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C72700 copper-nickel and the bottom bar is ASTM B563 Pd-Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 4.0 to 36 | |
| 7.0 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.37 |
| Shear Modulus, GPa | 44 | |
| 37 |
| Shear Strength, MPa | 310 to 620 | |
| 470 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1070 | |
| 760 to 1170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 150 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1180 |
| Melting Onset (Solidus), °C | 930 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 260 |
| Thermal Expansion, µm/m-K | 17 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 5.6 to 6.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 4.6 to 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 14 |
| Strength to Weight: Axial, points | 14 to 34 | |
| 19 to 30 |
| Strength to Weight: Bending, points | 15 to 26 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 16 to 38 | |
| 39 to 61 |
Alloy Composition
| Copper (Cu), % | 82.1 to 86 | |
| 15.5 to 16.5 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.3 | |
| 0 |
| Nickel (Ni), % | 8.5 to 9.5 | |
| 0.8 to 1.2 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 43 to 45 |
| Platinum (Pt), % | 0 | |
| 0.8 to 1.2 |
| Silver (Ag), % | 0 | |
| 37 to 39 |
| Tin (Sn), % | 5.5 to 6.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |