C72900 Copper-nickel vs. R05400 Tantalum
C72900 copper-nickel belongs to the copper alloys classification, while R05400 tantalum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C72900 copper-nickel and the bottom bar is R05400 tantalum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 6.0 to 20 | |
| 1.1 to 28 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1080 | |
| 210 to 540 |
| Tensile Strength: Yield (Proof), MPa | 700 to 920 | |
| 140 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 140 |
| Thermal Conductivity, W/m-K | 29 | |
| 59 |
| Thermal Expansion, µm/m-K | 17 | |
| 6.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 17 |
| Embodied Water, L/kg | 360 | |
| 650 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 210 | |
| 5.5 to 53 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2030 to 3490 | |
| 50 to 420 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 6.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 11 |
| Strength to Weight: Axial, points | 27 to 34 | |
| 3.6 to 9.0 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 4.8 to 8.8 |
| Thermal Diffusivity, mm2/s | 8.6 | |
| 25 |
| Thermal Shock Resistance, points | 31 to 38 | |
| 13 to 32 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 74.1 to 78 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 14.5 to 15.5 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 to 0.1 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Tantalum (Ta), % | 0 | |
| 99.7 to 100 |
| Tin (Sn), % | 7.5 to 8.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |