C72900 Copper-nickel vs. R60901 Alloy
C72900 copper-nickel belongs to the copper alloys classification, while R60901 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C72900 copper-nickel and the bottom bar is R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 98 |
| Elongation at Break, % | 6.0 to 20 | |
| 17 to 22 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1080 | |
| 500 to 580 |
| Tensile Strength: Yield (Proof), MPa | 700 to 920 | |
| 350 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 270 |
| Thermal Conductivity, W/m-K | 29 | |
| 17 |
| Thermal Expansion, µm/m-K | 17 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 6.6 |
| Embodied Water, L/kg | 360 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 210 | |
| 88 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2030 to 3490 | |
| 640 to 760 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 27 to 34 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 8.6 | |
| 9.7 |
| Thermal Shock Resistance, points | 31 to 38 | |
| 58 to 67 |
Alloy Composition
| Copper (Cu), % | 74.1 to 78 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 14.5 to 15.5 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 2.4 to 2.8 |
| Tin (Sn), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 96.8 to 97.5 |
| Residuals, % | 0 | |
| 0 to 0.29 |