C73500 Nickel Silver vs. C14700 Copper
Both C73500 nickel silver and C14700 copper are copper alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C73500 nickel silver and the bottom bar is C14700 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 47 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 580 | |
| 240 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 200 |
| Melting Completion (Liquidus), °C | 1140 | |
| 1080 |
| Melting Onset (Solidus), °C | 1090 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 36 | |
| 370 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.5 | |
| 95 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.7 | |
| 96 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 30 |
| Density, g/cm3 | 8.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 61 | |
| 41 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 7.3 to 10 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 9.5 to 12 |
| Thermal Diffusivity, mm2/s | 10 | |
| 110 |
| Thermal Shock Resistance, points | 13 to 19 | |
| 8.4 to 12 |
Alloy Composition
| Copper (Cu), % | 70.5 to 73.5 | |
| 99.395 to 99.798 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 16.5 to 19.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.0020 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0.2 to 0.5 |
| Zinc (Zn), % | 5.7 to 13 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |