C74500 Nickel Silver vs. ASTM A372 Grade M Steel
C74500 nickel silver belongs to the copper alloys classification, while ASTM A372 grade M steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C74500 nickel silver and the bottom bar is ASTM A372 grade M steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 3.0 to 24 | |
| 18 to 21 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 73 |
| Shear Strength, MPa | 310 to 380 | |
| 510 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 700 | |
| 810 to 910 |
| Tensile Strength: Yield (Proof), MPa | 380 to 600 | |
| 660 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 450 |
| Melting Completion (Liquidus), °C | 1020 | |
| 1460 |
| Melting Onset (Solidus), °C | 970 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 46 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 9.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 5.0 |
| Density, g/cm3 | 8.3 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.0 |
| Embodied Energy, MJ/kg | 54 | |
| 27 |
| Embodied Water, L/kg | 310 | |
| 61 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 160 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 to 1540 | |
| 1140 to 1580 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 23 | |
| 29 to 32 |
| Strength to Weight: Bending, points | 14 to 21 | |
| 24 to 27 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 13 to 23 | |
| 24 to 27 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.23 |
| Chromium (Cr), % | 0 | |
| 1.5 to 2.0 |
| Copper (Cu), % | 63.5 to 66.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 92.5 to 95.1 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0.4 to 0.6 |
| Nickel (Ni), % | 9.0 to 11 | |
| 2.8 to 3.9 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Vanadium (V), % | 0 | |
| 0 to 0.080 |
| Zinc (Zn), % | 21.2 to 27.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |