C74500 Nickel Silver vs. C33200 Brass
Both C74500 nickel silver and C33200 brass are copper alloys. They have 90% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C74500 nickel silver and the bottom bar is C33200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 3.0 to 24 | |
| 7.0 to 60 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Rockwell Superficial 30T Hardness | 60 to 79 | |
| 26 to 69 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Shear Strength, MPa | 310 to 380 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 700 | |
| 320 to 520 |
| Tensile Strength: Yield (Proof), MPa | 380 to 600 | |
| 110 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 130 |
| Melting Completion (Liquidus), °C | 1020 | |
| 930 |
| Melting Onset (Solidus), °C | 970 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 45 | |
| 120 |
| Thermal Expansion, µm/m-K | 19 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 24 |
| Density, g/cm3 | 8.3 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 54 | |
| 44 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 160 | |
| 35 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 to 1540 | |
| 60 to 960 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 13 to 23 | |
| 11 to 17 |
| Strength to Weight: Bending, points | 14 to 21 | |
| 13 to 17 |
| Thermal Diffusivity, mm2/s | 14 | |
| 37 |
| Thermal Shock Resistance, points | 13 to 23 | |
| 11 to 17 |
Alloy Composition
| Copper (Cu), % | 63.5 to 66.5 | |
| 65 to 68 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 to 0.1 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 |
| Zinc (Zn), % | 21.2 to 27.5 | |
| 29 to 33.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |