C75200 Nickel Silver vs. C19400 Copper
Both C75200 nickel silver and C19400 copper are copper alloys. They have 65% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C75200 nickel silver and the bottom bar is C19400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Rockwell Superficial 30T Hardness | 58 to 78 | |
| 59 to 78 |
| Shear Modulus, GPa | 47 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 660 | |
| 310 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1110 | |
| 1090 |
| Melting Onset (Solidus), °C | 1070 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 33 | |
| 260 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.0 | |
| 58 to 68 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.3 | |
| 58 to 69 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 30 |
| Density, g/cm3 | 8.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 2.6 |
| Embodied Energy, MJ/kg | 62 | |
| 40 |
| Embodied Water, L/kg | 300 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 9.7 to 20 |
| Strength to Weight: Bending, points | 14 to 20 | |
| 11 to 18 |
| Thermal Diffusivity, mm2/s | 9.8 | |
| 75 |
| Thermal Shock Resistance, points | 13 to 22 | |
| 11 to 22 |
Alloy Composition
| Copper (Cu), % | 63.5 to 66.5 | |
| 96.8 to 97.8 |
| Iron (Fe), % | 0 to 0.25 | |
| 2.1 to 2.6 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 16.5 to 19.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.015 to 0.15 |
| Zinc (Zn), % | 12.7 to 20 | |
| 0.050 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |