C75400 Nickel Silver vs. ASTM B617 Coin Silver
C75400 nickel silver belongs to the copper alloys classification, while ASTM B617 coin silver belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C75400 nickel silver and the bottom bar is ASTM B617 coin silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 75 |
| Elongation at Break, % | 2.0 to 43 | |
| 1.1 to 22 |
| Poisson's Ratio | 0.32 | |
| 0.37 |
| Shear Modulus, GPa | 46 | |
| 28 |
| Shear Strength, MPa | 250 to 370 | |
| 180 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 290 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 120 |
| Melting Completion (Liquidus), °C | 1080 | |
| 870 |
| Melting Onset (Solidus), °C | 1040 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 250 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 83 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.4 | |
| 72 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.9 | |
| 4.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 14 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 7.7 to 14 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 9.3 to 14 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 14 to 25 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 63.5 to 66.5 | |
| 9.0 to 10.4 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 14 to 16 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silver (Ag), % | 0 | |
| 89.6 to 91 |
| Zinc (Zn), % | 16.2 to 22.5 | |
| 0 to 0.060 |
| Residuals, % | 0 | |
| 0 to 0.060 |