C75400 Nickel Silver vs. C41300 Brass
Both C75400 nickel silver and C41300 brass are copper alloys. They have 73% of their average alloy composition in common.
For each property being compared, the top bar is C75400 nickel silver and the bottom bar is C41300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.0 to 43 | |
| 2.0 to 44 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Rockwell B Hardness | 60 to 90 | |
| 53 to 88 |
| Rockwell Superficial 30T Hardness | 27 to 77 | |
| 20 to 77 |
| Shear Modulus, GPa | 46 | |
| 42 |
| Shear Strength, MPa | 250 to 370 | |
| 230 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 300 to 630 |
| Tensile Strength: Yield (Proof), MPa | 130 to 590 | |
| 120 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1040 |
| Melting Onset (Solidus), °C | 1040 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 36 | |
| 130 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.4 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 29 |
| Density, g/cm3 | 8.5 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 59 | |
| 44 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 120 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 1450 | |
| 69 to 1440 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 9.6 to 20 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 11 to 19 |
| Thermal Diffusivity, mm2/s | 11 | |
| 40 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 11 to 22 |
Alloy Composition
| Copper (Cu), % | 63.5 to 66.5 | |
| 89 to 93 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 14 to 16 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.7 to 1.3 |
| Zinc (Zn), % | 16.2 to 22.5 | |
| 5.1 to 10.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |