C75400 Nickel Silver vs. C69300 Brass
Both C75400 nickel silver and C69300 brass are copper alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C75400 nickel silver and the bottom bar is C69300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.0 to 43 | |
| 8.5 to 15 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Rockwell B Hardness | 60 to 90 | |
| 84 to 88 |
| Shear Modulus, GPa | 46 | |
| 41 |
| Shear Strength, MPa | 250 to 370 | |
| 330 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 550 to 630 |
| Tensile Strength: Yield (Proof), MPa | 130 to 590 | |
| 300 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 160 |
| Melting Completion (Liquidus), °C | 1080 | |
| 880 |
| Melting Onset (Solidus), °C | 1040 | |
| 860 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 36 | |
| 38 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.4 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 26 |
| Density, g/cm3 | 8.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 59 | |
| 45 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 120 | |
| 47 to 70 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 1450 | |
| 400 to 700 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 19 to 21 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 12 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 19 to 22 |
Alloy Composition
| Copper (Cu), % | 63.5 to 66.5 | |
| 73 to 77 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.090 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 14 to 16 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 | |
| 0.040 to 0.15 |
| Silicon (Si), % | 0 | |
| 2.7 to 3.4 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 16.2 to 22.5 | |
| 18.4 to 24.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |