C77100 Nickel Silver vs. AWS E209

C77100 nickel silver belongs to the copper alloys classification, while AWS E209 belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is C77100 nickel silver and the bottom bar is AWS E209.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 45
79
Tensile Strength: Ultimate (UTS), MPa 600
770

Thermal Properties

Latent Heat of Fusion, J/g 180
300
Melting Completion (Liquidus), °C 990
1420
Melting Onset (Solidus), °C 950
1370
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 20
14

Otherwise Unclassified Properties

Base Metal Price, % relative 27
21
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 3.5
4.4
Embodied Energy, MJ/kg 56
63
Embodied Water, L/kg 310
180

Common Calculations

Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 21
28
Strength to Weight: Bending, points 20
24
Thermal Shock Resistance, points 19
19

Alloy Composition

Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
20.5 to 24
Copper (Cu), % 52 to 56
0 to 0.75
Iron (Fe), % 0
51.5 to 64.3
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.9
4.0 to 7.0
Molybdenum (Mo), % 0
1.5 to 3.0
Nickel (Ni), % 9.0 to 12
9.5 to 12
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
0.1 to 0.3
Zinc (Zn), % 30.6 to 39
0
Residuals, % 0 to 0.5
0