C77300 Nickel Silver vs. AWS ER80S-B6
C77300 nickel silver belongs to the copper alloys classification, while AWS ER80S-B6 belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C77300 nickel silver and the bottom bar is AWS ER80S-B6.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 260 |
| Melting Completion (Liquidus), °C | 940 | |
| 1460 |
| Melting Onset (Solidus), °C | 920 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.5 | |
| 8.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.3 | |
| 9.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 4.7 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 1.8 |
| Embodied Energy, MJ/kg | 56 | |
| 24 |
| Embodied Water, L/kg | 310 | |
| 71 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 19 | |
| 22 |
| Strength to Weight: Bending, points | 19 | |
| 21 |
| Thermal Shock Resistance, points | 17 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 4.5 to 6.0 |
| Copper (Cu), % | 46 to 50 | |
| 0 to 0.35 |
| Iron (Fe), % | 0 | |
| 90.6 to 94.7 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 0 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 to 0.6 |
| Phosphorus (P), % | 0 to 0.25 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.040 to 0.25 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Zinc (Zn), % | 37.9 to 45 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |