C77300 Nickel Silver vs. Grade CU5MCuC Nickel
C77300 nickel silver belongs to the copper alloys classification, while grade CU5MCuC nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C77300 nickel silver and the bottom bar is grade CU5MCuC nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 980 |
| Melting Completion (Liquidus), °C | 940 | |
| 1420 |
| Melting Onset (Solidus), °C | 920 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 460 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 45 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 7.7 |
| Embodied Energy, MJ/kg | 56 | |
| 110 |
| Embodied Water, L/kg | 310 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 20 |
| Strength to Weight: Bending, points | 19 | |
| 19 |
| Thermal Shock Resistance, points | 17 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 19.5 to 23.5 |
| Copper (Cu), % | 46 to 50 | |
| 1.5 to 3.5 |
| Iron (Fe), % | 0 | |
| 22.2 to 37.9 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 9.0 to 11 | |
| 38 to 44 |
| Niobium (Nb), % | 0 | |
| 0.6 to 1.2 |
| Phosphorus (P), % | 0 to 0.25 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.040 to 0.25 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 37.9 to 45 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |