C77400 Nickel Silver vs. C32000 Brass
Both C77400 nickel silver and C32000 brass are copper alloys. They have 58% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C77400 nickel silver and the bottom bar is C32000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 25 | |
| 6.8 to 29 |
| Poisson's Ratio | 0.3 | |
| 0.33 |
| Shear Modulus, GPa | 42 | |
| 41 |
| Shear Strength, MPa | 360 | |
| 180 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 270 to 470 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 78 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 170 |
| Melting Completion (Liquidus), °C | 810 | |
| 1020 |
| Melting Onset (Solidus), °C | 770 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Expansion, µm/m-K | 21 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 28 |
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 2.6 |
| Embodied Energy, MJ/kg | 57 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 30 to 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 28 to 680 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 20 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 19 | |
| 11 to 16 |
| Thermal Shock Resistance, points | 18 | |
| 9.5 to 16 |
Alloy Composition
| Copper (Cu), % | 43 to 47 | |
| 83.5 to 86.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.2 | |
| 1.5 to 2.2 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 to 0.25 |
| Zinc (Zn), % | 41.3 to 48 | |
| 10.6 to 15 |
| Residuals, % | 0 | |
| 0 to 0.4 |