C77600 Nickel Silver vs. 851.0 Aluminum

C77600 nickel silver belongs to the copper alloys classification, while 851.0 aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C77600 nickel silver and the bottom bar is 851.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
69
Elongation at Break, % 30
3.9 to 9.1
Poisson's Ratio 0.3
0.33
Shear Modulus, GPa 43
26
Tensile Strength: Ultimate (UTS), MPa 630
130 to 140

Thermal Properties

Latent Heat of Fusion, J/g 180
410
Maximum Temperature: Mechanical, °C 140
180
Melting Completion (Liquidus), °C 830
630
Melting Onset (Solidus), °C 790
360
Specific Heat Capacity, J/kg-K 390
850
Thermal Expansion, µm/m-K 20
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
46
Electrical Conductivity: Equal Weight (Specific), % IACS 31
140

Otherwise Unclassified Properties

Base Metal Price, % relative 27
14
Density, g/cm3 7.9
3.1
Embodied Carbon, kg CO2/kg material 3.7
8.4
Embodied Energy, MJ/kg 60
160
Embodied Water, L/kg 310
1140

Common Calculations

Stiffness to Weight: Axial, points 7.9
13
Stiffness to Weight: Bending, points 20
45
Strength to Weight: Axial, points 22
12 to 13
Strength to Weight: Bending, points 21
19 to 20
Thermal Shock Resistance, points 20
6.1 to 6.3

Alloy Composition

Aluminum (Al), % 0
86.6 to 91.5
Copper (Cu), % 42 to 45
0.7 to 1.3
Iron (Fe), % 0 to 0.2
0 to 0.7
Lead (Pb), % 0 to 0.25
0
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0 to 0.25
0 to 0.1
Nickel (Ni), % 12 to 14
0.3 to 0.7
Silicon (Si), % 0
2.0 to 3.0
Tin (Sn), % 0 to 0.15
5.5 to 7.0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 39.7 to 46
0
Residuals, % 0
0 to 0.3