C77600 Nickel Silver vs. C63600 Bronze
Both C77600 nickel silver and C63600 bronze are copper alloys. They have 44% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C77600 nickel silver and the bottom bar is C63600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 30 | |
| 30 to 66 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Rockwell B Hardness | 83 | |
| 71 to 84 |
| Shear Modulus, GPa | 43 | |
| 42 |
| Shear Strength, MPa | 410 | |
| 320 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 410 to 540 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 150 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 210 |
| Melting Completion (Liquidus), °C | 830 | |
| 1030 |
| Melting Onset (Solidus), °C | 790 | |
| 980 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 410 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 30 |
| Density, g/cm3 | 7.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 3.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 60 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 98 to 290 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 470 | |
| 100 to 300 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 22 | |
| 13 to 18 |
| Strength to Weight: Bending, points | 21 | |
| 14 to 17 |
| Thermal Shock Resistance, points | 20 | |
| 15 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Arsenic (As), % | 0 | |
| 0 to 0.15 |
| Copper (Cu), % | 42 to 45 | |
| 93 to 96.3 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.25 | |
| 0 |
| Nickel (Ni), % | 12 to 14 | |
| 0 to 0.15 |
| Silicon (Si), % | 0 | |
| 0.7 to 1.3 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 to 0.2 |
| Zinc (Zn), % | 39.7 to 46 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |