C77600 Nickel Silver vs. R60704 Alloy

C77600 nickel silver belongs to the copper alloys classification, while R60704 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C77600 nickel silver and the bottom bar is R60704 alloy.

UNS C77600 Nickel Silver UNS R60704 Zirconium-Tin Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		97

Elongation at Break, %		30
Elongation at Break, %		16

Poisson's Ratio		0.3
Poisson's Ratio		0.34

Shear Modulus, GPa		43
Shear Modulus, GPa		36

Tensile Strength: Ultimate (UTS), MPa		630
Tensile Strength: Ultimate (UTS), MPa		470

Tensile Strength: Yield (Proof), MPa		320
Tensile Strength: Yield (Proof), MPa		270

Thermal Properties

Latent Heat of Fusion, J/g		180
Latent Heat of Fusion, J/g		240

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		270

Thermal Expansion, µm/m-K		20
Thermal Expansion, µm/m-K		6.0

Otherwise Unclassified Properties

Density, g/cm³		7.9
Density, g/cm³		6.7

Embodied Water, L/kg		310
Embodied Water, L/kg		460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		160
Resilience: Ultimate (Unit Rupture Work), MJ/m³		64

Resilience: Unit (Modulus of Resilience), kJ/m³		470
Resilience: Unit (Modulus of Resilience), kJ/m³		370

Stiffness to Weight: Axial, points		7.9
Stiffness to Weight: Axial, points		8.1

Stiffness to Weight: Bending, points		20
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		20

Strength to Weight: Bending, points		21
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		20
Thermal Shock Resistance, points		58

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.050

Chromium (Cr), %		0
Chromium (Cr), %		0.2 to 0.4

Copper (Cu), %		42 to 45
Copper (Cu), %		0

Hafnium (Hf), %		0
Hafnium (Hf), %		0 to 4.5

Hydrogen (H), %		0
Hydrogen (H), %		0 to 0.0050

Iron (Fe), %		0 to 0.2
Iron (Fe), %		0.2 to 0.4

Lead (Pb), %		0 to 0.25
Lead (Pb), %		0

Manganese (Mn), %		0 to 0.25
Manganese (Mn), %		0

Nickel (Ni), %		12 to 14
Nickel (Ni), %		0

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.025

Oxygen (O), %		0
Oxygen (O), %		0 to 0.18

Tin (Sn), %		0 to 0.15
Tin (Sn), %		1.0 to 2.0

Zinc (Zn), %		39.7 to 46
Zinc (Zn), %		0

Zirconium (Zr), %		0
Zirconium (Zr), %		93 to 98.8

Residuals, %		0 to 0.5
Residuals, %		0