C78200 Nickel Silver vs. C67400 Bronze
Both C78200 nickel silver and C67400 bronze are copper alloys. They have 84% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C78200 nickel silver and the bottom bar is C67400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 3.0 to 40 | |
| 22 to 28 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Rockwell B Hardness | 65 to 90 | |
| 78 to 85 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Shear Strength, MPa | 280 to 400 | |
| 310 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 480 to 610 |
| Tensile Strength: Yield (Proof), MPa | 170 to 570 | |
| 250 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 130 |
| Melting Completion (Liquidus), °C | 1000 | |
| 890 |
| Melting Onset (Solidus), °C | 970 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 48 | |
| 100 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 23 |
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 2.8 |
| Embodied Energy, MJ/kg | 52 | |
| 48 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 120 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1440 | |
| 300 to 660 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 17 to 22 |
| Strength to Weight: Bending, points | 14 to 19 | |
| 17 to 20 |
| Thermal Diffusivity, mm2/s | 15 | |
| 32 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 16 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.5 to 2.0 |
| Copper (Cu), % | 63 to 67 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.35 |
| Lead (Pb), % | 1.5 to 2.5 | |
| 0 to 0.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 2.0 to 3.5 |
| Nickel (Ni), % | 7.0 to 9.0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 | |
| 0.5 to 1.5 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 20.2 to 28.5 | |
| 31.1 to 40 |
| Residuals, % | 0 | |
| 0 to 0.5 |