C78200 Nickel Silver vs. C74500 Nickel Silver
Both C78200 nickel silver and C74500 nickel silver are copper alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is C78200 nickel silver and the bottom bar is C74500 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 3.0 to 40 | |
| 3.0 to 24 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Rockwell B Hardness | 65 to 90 | |
| 66 to 94 |
| Rockwell Superficial 30T Hardness | 63 to 75 | |
| 60 to 79 |
| Shear Modulus, GPa | 43 | |
| 44 |
| Shear Strength, MPa | 280 to 400 | |
| 310 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 390 to 700 |
| Tensile Strength: Yield (Proof), MPa | 170 to 570 | |
| 380 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 170 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1020 |
| Melting Onset (Solidus), °C | 970 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 48 | |
| 45 |
| Thermal Expansion, µm/m-K | 19 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 9.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 29 |
| Density, g/cm3 | 8.4 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 3.4 |
| Embodied Energy, MJ/kg | 52 | |
| 54 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 120 | |
| 12 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1440 | |
| 620 to 1540 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 13 to 23 |
| Strength to Weight: Bending, points | 14 to 19 | |
| 14 to 21 |
| Thermal Diffusivity, mm2/s | 15 | |
| 14 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 13 to 23 |
Alloy Composition
| Copper (Cu), % | 63 to 67 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.25 |
| Lead (Pb), % | 1.5 to 2.5 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 7.0 to 9.0 | |
| 9.0 to 11 |
| Zinc (Zn), % | 20.2 to 28.5 | |
| 21.2 to 27.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |