C79200 Nickel Silver vs. ACI-ASTM CE3MN Steel

C79200 nickel silver belongs to the copper alloys classification, while ACI-ASTM CE3MN steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C79200 nickel silver and the bottom bar is ACI-ASTM CE3MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
210
Poisson's Ratio 0.32
0.27
Shear Modulus, GPa 44
81
Tensile Strength: Ultimate (UTS), MPa 480 to 540
770

Thermal Properties

Latent Heat of Fusion, J/g 190
300
Maximum Temperature: Mechanical, °C 170
1100
Melting Completion (Liquidus), °C 950
1450
Melting Onset (Solidus), °C 910
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 42
15
Thermal Expansion, µm/m-K 19
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 30
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 30
21
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 3.6
4.2
Embodied Energy, MJ/kg 56
58
Embodied Water, L/kg 310
180

Common Calculations

Stiffness to Weight: Axial, points 7.7
15
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 16 to 18
27
Strength to Weight: Bending, points 16 to 18
24
Thermal Diffusivity, mm2/s 13
4.1
Thermal Shock Resistance, points 16 to 18
21

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 59 to 66.5
0
Iron (Fe), % 0 to 0.25
58.1 to 65.9
Lead (Pb), % 0.8 to 1.4
0
Manganese (Mn), % 0 to 0.5
0 to 1.5
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 11 to 13
6.0 to 8.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 17.9 to 29.2
0
Residuals, % 0 to 0.5
0