C79200 Nickel Silver vs. AWS E33-31

C79200 nickel silver belongs to the copper alloys classification, while AWS E33-31 belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C79200 nickel silver and the bottom bar is AWS E33-31.

UNS C79200 (CW404J) Leaded Nickel Silver AWS E33-31 (W33310) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		210

Poisson's Ratio		0.32
Poisson's Ratio		0.27

Shear Modulus, GPa		44
Shear Modulus, GPa		81

Tensile Strength: Ultimate (UTS), MPa		480 to 540
Tensile Strength: Ultimate (UTS), MPa		810

Thermal Properties

Latent Heat of Fusion, J/g		190
Latent Heat of Fusion, J/g		320

Melting Completion (Liquidus), °C		950
Melting Completion (Liquidus), °C		1380

Melting Onset (Solidus), °C		910
Melting Onset (Solidus), °C		1330

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		30
Base Metal Price, % relative		36

Density, g/cm³		8.4
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		6.0

Embodied Energy, MJ/kg		56
Embodied Energy, MJ/kg		86

Embodied Water, L/kg		310
Embodied Water, L/kg		260

Common Calculations

Stiffness to Weight: Axial, points		7.7
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		16 to 18
Strength to Weight: Axial, points		28

Strength to Weight: Bending, points		16 to 18
Strength to Weight: Bending, points		24

Thermal Shock Resistance, points		16 to 18
Thermal Shock Resistance, points		19

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.030

Chromium (Cr), %		0
Chromium (Cr), %		31 to 35

Copper (Cu), %		59 to 66.5
Copper (Cu), %		0.4 to 0.8

Iron (Fe), %		0 to 0.25
Iron (Fe), %		24.7 to 34.8

Lead (Pb), %		0.8 to 1.4
Lead (Pb), %		0

Manganese (Mn), %		0 to 0.5
Manganese (Mn), %		2.5 to 4.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		1.0 to 2.0

Nickel (Ni), %		11 to 13
Nickel (Ni), %		30 to 32

Nitrogen (N), %		0
Nitrogen (N), %		0.3 to 0.5

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0
Sulfur (S), %		0 to 0.010

Zinc (Zn), %		17.9 to 29.2
Zinc (Zn), %		0

Residuals, %		0 to 0.5
Residuals, %		0