C79200 Nickel Silver vs. AWS ERTi-7
C79200 nickel silver belongs to the copper alloys classification, while AWS ERTi-7 belongs to the titanium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C79200 nickel silver and the bottom bar is AWS ERTi-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 540 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 320 |
| Melting Completion (Liquidus), °C | 950 | |
| 1670 |
| Melting Onset (Solidus), °C | 910 | |
| 1620 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 540 |
| Thermal Conductivity, W/m-K | 42 | |
| 21 |
| Thermal Expansion, µm/m-K | 19 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 30 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 47 |
| Embodied Energy, MJ/kg | 56 | |
| 800 |
| Embodied Water, L/kg | 310 | |
| 470 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 35 |
| Strength to Weight: Axial, points | 16 to 18 | |
| 21 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 24 |
| Thermal Diffusivity, mm2/s | 13 | |
| 8.8 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 26 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Copper (Cu), % | 59 to 66.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0080 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.12 |
| Lead (Pb), % | 0.8 to 1.4 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 11 to 13 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.015 |
| Oxygen (O), % | 0 | |
| 0.080 to 0.16 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.25 |
| Titanium (Ti), % | 0 | |
| 99.417 to 99.8 |
| Zinc (Zn), % | 17.9 to 29.2 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |