C79200 Nickel Silver vs. CC499K Bronze

Both C79200 nickel silver and CC499K bronze are copper alloys. They have 69% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C79200 nickel silver and the bottom bar is CC499K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 44
41
Tensile Strength: Ultimate (UTS), MPa 480 to 540
260

Thermal Properties

Latent Heat of Fusion, J/g 190
190
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 950
1000
Melting Onset (Solidus), °C 910
920
Specific Heat Capacity, J/kg-K 390
370
Thermal Conductivity, W/m-K 42
73
Thermal Expansion, µm/m-K 19
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
12
Electrical Conductivity: Equal Weight (Specific), % IACS 30
12

Otherwise Unclassified Properties

Base Metal Price, % relative 30
32
Density, g/cm3 8.4
8.8
Embodied Carbon, kg CO2/kg material 3.6
3.1
Embodied Energy, MJ/kg 56
51
Embodied Water, L/kg 310
350

Common Calculations

Stiffness to Weight: Axial, points 7.7
6.9
Stiffness to Weight: Bending, points 19
18
Strength to Weight: Axial, points 16 to 18
8.1
Strength to Weight: Bending, points 16 to 18
10
Thermal Diffusivity, mm2/s 13
22
Thermal Shock Resistance, points 16 to 18
9.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.020
Cadmium (Cd), % 0
0 to 0.020
Chromium (Cr), % 0
0 to 0.020
Copper (Cu), % 59 to 66.5
84 to 88
Iron (Fe), % 0 to 0.25
0 to 0.3
Lead (Pb), % 0.8 to 1.4
0 to 3.0
Manganese (Mn), % 0 to 0.5
0
Nickel (Ni), % 11 to 13
0 to 0.6
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 0.010
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0
4.0 to 6.0
Zinc (Zn), % 17.9 to 29.2
4.0 to 6.0
Residuals, % 0 to 0.5
0