C79600 Nickel Silver vs. ASTM B617 Coin Silver

C79600 nickel silver belongs to the copper alloys classification, while ASTM B617 coin silver belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is ASTM B617 coin silver.

UNS C79600 Leaded Nickel Silver ASTM B617 Coin Silver Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		75

Elongation at Break, %		15
Elongation at Break, %		1.1 to 22

Poisson's Ratio		0.3
Poisson's Ratio		0.37

Shear Modulus, GPa		43
Shear Modulus, GPa		28

Shear Strength, MPa		290
Shear Strength, MPa		180 to 290

Tensile Strength: Ultimate (UTS), MPa		480
Tensile Strength: Ultimate (UTS), MPa		290 to 520

Thermal Properties

Latent Heat of Fusion, J/g		180
Latent Heat of Fusion, J/g		120

Melting Completion (Liquidus), °C		930
Melting Completion (Liquidus), °C		870

Melting Onset (Solidus), °C		880
Melting Onset (Solidus), °C		780

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		250

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		7.0
Electrical Conductivity: Equal Volume, % IACS		83

Electrical Conductivity: Equal Weight (Specific), % IACS		8.0
Electrical Conductivity: Equal Weight (Specific), % IACS		72

Otherwise Unclassified Properties

Density, g/cm³		7.9
Density, g/cm³		10

Common Calculations

Stiffness to Weight: Axial, points		7.8
Stiffness to Weight: Axial, points		4.1

Stiffness to Weight: Bending, points		20
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		7.7 to 14

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		9.3 to 14

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		14 to 25

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		43.5 to 46.5
Copper (Cu), %		9.0 to 10.4

Iron (Fe), %		0
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0.8 to 1.2
Lead (Pb), %		0 to 0.030

Manganese (Mn), %		1.5 to 2.5
Manganese (Mn), %		0

Nickel (Ni), %		9.0 to 11
Nickel (Ni), %		0 to 0.010

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silver (Ag), %		0
Silver (Ag), %		89.6 to 91

Zinc (Zn), %		38.3 to 45.2
Zinc (Zn), %		0 to 0.060

Residuals, %		0
Residuals, %		0 to 0.060