C81400 Copper vs. Grade FDC Steel
C81400 copper belongs to the copper alloys classification, while grade FDC steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C81400 copper and the bottom bar is grade FDC steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 370 | |
| 1680 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1450 |
| Melting Onset (Solidus), °C | 1070 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 260 | |
| 51 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 60 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 61 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 1.9 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 45 | |
| 19 |
| Embodied Water, L/kg | 310 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 11 | |
| 60 |
| Strength to Weight: Bending, points | 13 | |
| 40 |
| Thermal Diffusivity, mm2/s | 75 | |
| 14 |
| Thermal Shock Resistance, points | 13 | |
| 50 |
Alloy Composition
| Beryllium (Be), % | 0.020 to 0.1 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 0.6 to 1.0 | |
| 0 to 0.3 |
| Copper (Cu), % | 98.4 to 99.38 | |
| 0 to 0.12 |
| Iron (Fe), % | 0 | |
| 98 to 99.4 |
| Manganese (Mn), % | 0 | |
| 0.5 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.1 to 0.35 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Residuals, % | 0 to 0.5 | |
| 0 |