C81500 Copper vs. Titanium 6-6-2
C81500 copper belongs to the copper alloys classification, while titanium 6-6-2 belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C81500 copper and the bottom bar is titanium 6-6-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 17 | |
| 6.7 to 9.0 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 44 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 1140 to 1370 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 1040 to 1230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 310 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1610 |
| Melting Onset (Solidus), °C | 1080 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 540 |
| Thermal Conductivity, W/m-K | 320 | |
| 5.5 |
| Thermal Expansion, µm/m-K | 17 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 82 | |
| 1.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 83 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 40 |
| Density, g/cm3 | 8.9 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 29 |
| Embodied Energy, MJ/kg | 41 | |
| 470 |
| Embodied Water, L/kg | 310 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 89 to 99 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 34 |
| Strength to Weight: Axial, points | 11 | |
| 66 to 79 |
| Strength to Weight: Bending, points | 12 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 91 | |
| 2.1 |
| Thermal Shock Resistance, points | 12 | |
| 75 to 90 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 5.0 to 6.0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.4 to 1.5 | |
| 0 |
| Copper (Cu), % | 97.4 to 99.6 | |
| 0.35 to 1.0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.1 | |
| 0.35 to 1.0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 5.0 to 6.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 |
| Tin (Sn), % | 0 to 0.1 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 82.8 to 87.8 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |