C82200 Copper vs. ASTM B685 Alloy

C82200 copper belongs to the copper alloys classification, while ASTM B685 alloy belongs to the otherwise unclassified metals. They have 40% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C82200 copper and the bottom bar is ASTM B685 alloy.

UNS C82200 (Alloy 14C) Nickel-Beryllium Copper ASTM B685 Palladium-Copper Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.34
Poisson's Ratio		0.37

Shear Modulus, GPa		44
Shear Modulus, GPa		43

Tensile Strength: Ultimate (UTS), MPa		390 to 660
Tensile Strength: Ultimate (UTS), MPa		660 to 1060

Thermal Properties

Latent Heat of Fusion, J/g		220
Latent Heat of Fusion, J/g		180

Melting Completion (Liquidus), °C		1080
Melting Completion (Liquidus), °C		1230

Melting Onset (Solidus), °C		1040
Melting Onset (Solidus), °C		1200

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		300

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		45
Electrical Conductivity: Equal Volume, % IACS		5.0

Electrical Conductivity: Equal Weight (Specific), % IACS		46
Electrical Conductivity: Equal Weight (Specific), % IACS		4.1

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		11

Common Calculations

Stiffness to Weight: Axial, points		7.4
Stiffness to Weight: Axial, points		6.1

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		15

Strength to Weight: Axial, points		12 to 20
Strength to Weight: Axial, points		17 to 27

Strength to Weight: Bending, points		13 to 19
Strength to Weight: Bending, points		16 to 21

Thermal Shock Resistance, points		14 to 23
Thermal Shock Resistance, points		28 to 46

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Beryllium (Be), %		0.35 to 0.8
Beryllium (Be), %		0

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Cobalt (Co), %		0 to 0.3
Cobalt (Co), %		0

Copper (Cu), %		97.4 to 98.7
Copper (Cu), %		39.5 to 40.5

Iron (Fe), %		0
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0
Lead (Pb), %		0 to 0.030

Nickel (Ni), %		1.0 to 2.0
Nickel (Ni), %		0

Palladium (Pd), %		0
Palladium (Pd), %		59 to 60.5

Silver (Ag), %		0
Silver (Ag), %		0 to 0.1

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.060

Residuals, %		0
Residuals, %		0 to 0.2