C82700 Copper vs. AWS E310H
C82700 copper belongs to the copper alloys classification, while AWS E310H belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C82700 copper and the bottom bar is AWS E310H.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 1.8 | |
| 11 |
| Poisson's Ratio | 0.33 | |
| 0.27 |
| Shear Modulus, GPa | 46 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 1200 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 300 |
| Melting Completion (Liquidus), °C | 950 | |
| 1400 |
| Melting Onset (Solidus), °C | 860 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Conductivity, W/m-K | 130 | |
| 14 |
| Thermal Expansion, µm/m-K | 17 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 20 | |
| 2.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 21 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 4.6 |
| Embodied Energy, MJ/kg | 180 | |
| 65 |
| Embodied Water, L/kg | 310 | |
| 200 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 38 | |
| 25 |
| Strength to Weight: Bending, points | 29 | |
| 22 |
| Thermal Diffusivity, mm2/s | 39 | |
| 3.8 |
| Thermal Shock Resistance, points | 41 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.15 | |
| 0 |
| Beryllium (Be), % | 2.4 to 2.6 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 0 to 0.090 | |
| 25 to 28 |
| Copper (Cu), % | 94.6 to 96.7 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 to 0.25 | |
| 44.2 to 53.7 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 1.0 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 1.0 to 1.5 | |
| 20 to 22.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |