C82700 Copper vs. N10629 Nickel
C82700 copper belongs to the copper alloys classification, while N10629 nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C82700 copper and the bottom bar is N10629 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 220 |
| Elongation at Break, % | 1.8 | |
| 45 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 46 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 1200 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 1020 | |
| 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 300 | |
| 910 |
| Melting Completion (Liquidus), °C | 950 | |
| 1610 |
| Melting Onset (Solidus), °C | 860 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Expansion, µm/m-K | 17 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 15 |
| Embodied Energy, MJ/kg | 180 | |
| 190 |
| Embodied Water, L/kg | 310 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 4260 | |
| 360 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 22 |
| Strength to Weight: Axial, points | 38 | |
| 26 |
| Strength to Weight: Bending, points | 29 | |
| 22 |
| Thermal Shock Resistance, points | 41 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.15 | |
| 0.1 to 0.5 |
| Beryllium (Be), % | 2.4 to 2.6 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 to 0.090 | |
| 0.5 to 1.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 94.6 to 96.7 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 1.0 to 6.0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 26 to 30 |
| Nickel (Ni), % | 1.0 to 1.5 | |
| 65 to 72.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |