C82800 Copper vs. ASTM A210 Steel
C82800 copper belongs to the copper alloys classification, while ASTM A210 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C82800 copper and the bottom bar is ASTM A210 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 1.0 to 20 | |
| 34 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 46 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1140 | |
| 470 to 540 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1000 | |
| 290 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 400 |
| Melting Completion (Liquidus), °C | 930 | |
| 1460 to 1470 |
| Melting Onset (Solidus), °C | 890 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 52 to 53 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 8.0 to 8.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 1.4 |
| Embodied Energy, MJ/kg | 190 | |
| 18 |
| Embodied Water, L/kg | 310 | |
| 45 to 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 110 | |
| 140 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 4080 | |
| 230 to 250 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 17 to 19 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 36 | |
| 14 |
| Thermal Shock Resistance, points | 23 to 39 | |
| 15 to 17 |