C84000 Brass vs. S30601 Stainless Steel
C84000 brass belongs to the copper alloys classification, while S30601 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C84000 brass and the bottom bar is S30601 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 65 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 27 | |
| 37 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 250 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 950 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1360 |
| Melting Onset (Solidus), °C | 940 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 500 |
| Thermal Expansion, µm/m-K | 18 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 20 |
| Density, g/cm3 | 8.6 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.9 |
| Embodied Energy, MJ/kg | 49 | |
| 55 |
| Embodied Water, L/kg | 330 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 58 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 83 | |
| 230 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 8.2 | |
| 24 |
| Strength to Weight: Bending, points | 10 | |
| 22 |
| Thermal Shock Resistance, points | 9.0 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.020 | |
| 0 |
| Boron (B), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.015 |
| Chromium (Cr), % | 0 | |
| 17 to 18 |
| Copper (Cu), % | 82 to 89 | |
| 0 to 0.35 |
| Iron (Fe), % | 0 to 0.4 | |
| 56.9 to 60.5 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0.5 to 2.0 | |
| 17 to 18 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.0050 | |
| 5.0 to 5.6 |
| Sulfur (S), % | 0.1 to 0.65 | |
| 0 to 0.013 |
| Tin (Sn), % | 2.0 to 4.0 | |
| 0 |
| Zinc (Zn), % | 5.0 to 14 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.7 | |
| 0 |