C84000 Brass vs. S31254 Stainless Steel

C84000 brass belongs to the copper alloys classification, while S31254 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is S31254 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
190
Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 27
40
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 42
80
Tensile Strength: Ultimate (UTS), MPa 250
720
Tensile Strength: Yield (Proof), MPa 140
330

Thermal Properties

Latent Heat of Fusion, J/g 190
300
Maximum Temperature: Mechanical, °C 170
1090
Melting Completion (Liquidus), °C 1040
1460
Melting Onset (Solidus), °C 940
1420
Specific Heat Capacity, J/kg-K 380
460
Thermal Conductivity, W/m-K 72
14
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 17
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 30
28
Density, g/cm3 8.6
8.0
Embodied Carbon, kg CO2/kg material 3.0
5.5
Embodied Energy, MJ/kg 49
74
Embodied Water, L/kg 330
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
240
Resilience: Unit (Modulus of Resilience), kJ/m3 83
270
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 8.2
25
Strength to Weight: Bending, points 10
22
Thermal Diffusivity, mm2/s 22
3.8
Thermal Shock Resistance, points 9.0
15

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
19.5 to 20.5
Copper (Cu), % 82 to 89
0.5 to 1.0
Iron (Fe), % 0 to 0.4
51.4 to 56.3
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0 to 1.0
Molybdenum (Mo), % 0
6.0 to 6.5
Nickel (Ni), % 0.5 to 2.0
17.5 to 18.5
Nitrogen (N), % 0
0.18 to 0.22
Phosphorus (P), % 0 to 0.050
0 to 0.030
Silicon (Si), % 0 to 0.0050
0 to 0.8
Sulfur (S), % 0.1 to 0.65
0 to 0.010
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0