C84500 Brass vs. SAE-AISI O2 Steel
C84500 brass belongs to the copper alloys classification, while SAE-AISI O2 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C84500 brass and the bottom bar is SAE-AISI O2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 39 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 640 to 2050 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 250 |
| Melting Completion (Liquidus), °C | 980 | |
| 1450 |
| Melting Onset (Solidus), °C | 840 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 470 |
| Thermal Conductivity, W/m-K | 72 | |
| 43 |
| Thermal Expansion, µm/m-K | 19 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 16 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 2.4 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.8 |
| Embodied Energy, MJ/kg | 47 | |
| 26 |
| Embodied Water, L/kg | 340 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 7.7 | |
| 23 to 73 |
| Strength to Weight: Bending, points | 9.8 | |
| 21 to 46 |
| Thermal Diffusivity, mm2/s | 23 | |
| 12 |
| Thermal Shock Resistance, points | 8.6 | |
| 22 to 70 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.85 to 1.0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 77 to 79 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.4 | |
| 95 to 97.8 |
| Lead (Pb), % | 6.0 to 7.5 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 1.4 to 1.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.030 |
| Tin (Sn), % | 2.0 to 4.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 10 to 14 | |
| 0 |
| Residuals, % | 0 to 0.7 | |
| 0 |