C85200 Brass vs. EN 1.5536 Steel

C85200 brass belongs to the copper alloys classification, while EN 1.5536 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C85200 brass and the bottom bar is EN 1.5536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
73
Tensile Strength: Ultimate (UTS), MPa 270
460 to 1600

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 140
400
Melting Completion (Liquidus), °C 940
1460
Melting Onset (Solidus), °C 930
1420
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 84
49
Thermal Expansion, µm/m-K 20
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 18
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 19
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 26
1.9
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.4
Embodied Energy, MJ/kg 46
19
Embodied Water, L/kg 330
48

Common Calculations

Stiffness to Weight: Axial, points 7.0
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 8.9
16 to 57
Strength to Weight: Bending, points 11
17 to 39
Thermal Diffusivity, mm2/s 27
13
Thermal Shock Resistance, points 9.3
14 to 47

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.2
0
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.25 to 0.3
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 70 to 74
0 to 0.25
Iron (Fe), % 0 to 0.6
97.6 to 98.7
Lead (Pb), % 1.5 to 3.8
0
Manganese (Mn), % 0
0.9 to 1.2
Nickel (Ni), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.050
0.15 to 0.3
Sulfur (S), % 0 to 0.050
0 to 0.025
Tin (Sn), % 0.7 to 2.0
0
Zinc (Zn), % 20 to 27
0
Residuals, % 0 to 0.9
0