C86100 Bronze vs. 7475 Aluminum
C86100 bronze belongs to the copper alloys classification, while 7475 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C86100 bronze and the bottom bar is 7475 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 70 |
| Elongation at Break, % | 20 | |
| 10 to 12 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 530 to 590 |
| Tensile Strength: Yield (Proof), MPa | 350 | |
| 440 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 180 |
| Melting Completion (Liquidus), °C | 940 | |
| 640 |
| Melting Onset (Solidus), °C | 900 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 870 |
| Thermal Conductivity, W/m-K | 35 | |
| 140 to 160 |
| Thermal Expansion, µm/m-K | 20 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 33 to 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.0 | |
| 98 to 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 10 |
| Density, g/cm3 | 8.0 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 8.2 |
| Embodied Energy, MJ/kg | 49 | |
| 150 |
| Embodied Water, L/kg | 350 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 53 to 68 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 530 | |
| 1390 to 1920 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 46 |
| Strength to Weight: Axial, points | 23 | |
| 49 to 55 |
| Strength to Weight: Bending, points | 21 | |
| 48 to 52 |
| Thermal Diffusivity, mm2/s | 10 | |
| 53 to 63 |
| Thermal Shock Resistance, points | 21 | |
| 23 to 26 |
Alloy Composition
| Aluminum (Al), % | 4.5 to 5.5 | |
| 88.6 to 91.6 |
| Chromium (Cr), % | 0 | |
| 0.18 to 0.25 |
| Copper (Cu), % | 66 to 68 | |
| 1.2 to 1.9 |
| Iron (Fe), % | 2.0 to 4.0 | |
| 0 to 0.12 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 1.9 to 2.6 |
| Manganese (Mn), % | 2.5 to 5.0 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.060 |
| Zinc (Zn), % | 17.3 to 25 | |
| 5.1 to 6.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |