C86500 Bronze vs. C87500 Brass

Both C86500 bronze and C87500 brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 72% of their average alloy composition in common.

For each property being compared, the top bar is C86500 bronze and the bottom bar is C87500 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 25
18
Poisson's Ratio 0.3
0.33
Shear Modulus, GPa 40
42
Tensile Strength: Ultimate (UTS), MPa 530
460
Tensile Strength: Yield (Proof), MPa 190
190

Thermal Properties

Latent Heat of Fusion, J/g 170
260
Maximum Temperature: Mechanical, °C 120
170
Melting Completion (Liquidus), °C 880
920
Melting Onset (Solidus), °C 860
820
Specific Heat Capacity, J/kg-K 390
410
Thermal Conductivity, W/m-K 86
28
Thermal Expansion, µm/m-K 21
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
6.7
Electrical Conductivity: Equal Weight (Specific), % IACS 25
7.3

Otherwise Unclassified Properties

Base Metal Price, % relative 23
27
Density, g/cm3 7.9
8.3
Embodied Carbon, kg CO2/kg material 2.8
2.7
Embodied Energy, MJ/kg 48
44
Embodied Water, L/kg 330
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
67
Resilience: Unit (Modulus of Resilience), kJ/m3 180
160
Stiffness to Weight: Axial, points 7.4
7.4
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 19
16
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 28
8.3
Thermal Shock Resistance, points 17
17

Alloy Composition

Aluminum (Al), % 0.5 to 1.5
0 to 0.5
Copper (Cu), % 55 to 60
79 to 85
Iron (Fe), % 0.4 to 2.0
0
Lead (Pb), % 0 to 0.4
0 to 0.5
Manganese (Mn), % 0.1 to 1.5
0
Nickel (Ni), % 0 to 1.0
0
Silicon (Si), % 0
3.0 to 5.0
Tin (Sn), % 0 to 1.0
0
Zinc (Zn), % 36 to 42
12 to 16
Residuals, % 0
0 to 0.5