C86800 Bronze vs. EN 1.4571 Stainless Steel
C86800 bronze belongs to the copper alloys classification, while EN 1.4571 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C86800 bronze and the bottom bar is EN 1.4571 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 22 | |
| 14 to 40 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 600 to 900 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 230 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 950 |
| Melting Completion (Liquidus), °C | 900 | |
| 1440 |
| Melting Onset (Solidus), °C | 880 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 19 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.9 |
| Embodied Energy, MJ/kg | 51 | |
| 54 |
| Embodied Water, L/kg | 320 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 110 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 | |
| 130 to 820 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 19 | |
| 20 to 26 |
| Thermal Shock Resistance, points | 18 | |
| 13 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 2.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 53.5 to 57 | |
| 0 |
| Iron (Fe), % | 1.0 to 2.5 | |
| 61.7 to 71 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 2.5 to 4.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.0 to 2.5 |
| Nickel (Ni), % | 2.5 to 4.0 | |
| 10.5 to 13.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.7 |
| Zinc (Zn), % | 28.3 to 40.5 | |
| 0 |
| Residuals, % | 0 to 1.0 | |
| 0 |