C86800 Bronze vs. SAE-AISI S1 Steel
C86800 bronze belongs to the copper alloys classification, while SAE-AISI S1 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C86800 bronze and the bottom bar is SAE-AISI S1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 690 to 1840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 260 |
| Melting Completion (Liquidus), °C | 900 | |
| 1500 |
| Melting Onset (Solidus), °C | 880 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 8.0 |
| Density, g/cm3 | 7.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 51 | |
| 37 |
| Embodied Water, L/kg | 320 | |
| 56 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 24 to 64 |
| Strength to Weight: Bending, points | 19 | |
| 22 to 42 |
| Thermal Shock Resistance, points | 18 | |
| 21 to 56 |
Alloy Composition
| Aluminum (Al), % | 0 to 2.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.4 to 0.55 |
| Chromium (Cr), % | 0 | |
| 1.0 to 1.8 |
| Copper (Cu), % | 53.5 to 57 | |
| 0 to 0.25 |
| Iron (Fe), % | 1.0 to 2.5 | |
| 91.6 to 96.7 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 2.5 to 4.0 | |
| 0.1 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 2.5 to 4.0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.15 to 1.2 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Tungsten (W), % | 0 | |
| 1.5 to 3.0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.3 |
| Zinc (Zn), % | 28.3 to 40.5 | |
| 0 |
| Residuals, % | 0 to 1.0 | |
| 0 |