C90200 Bronze vs. EN 1.5701 Steel

C90200 bronze belongs to the copper alloys classification, while EN 1.5701 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C90200 bronze and the bottom bar is EN 1.5701 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 70
130 to 160
Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 41
73
Tensile Strength: Ultimate (UTS), MPa 260
430 to 1300

Thermal Properties

Latent Heat of Fusion, J/g 200
250
Maximum Temperature: Mechanical, °C 180
410
Melting Completion (Liquidus), °C 1050
1460
Melting Onset (Solidus), °C 880
1420
Specific Heat Capacity, J/kg-K 370
470
Thermal Conductivity, W/m-K 62
45
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 13
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 34
2.4
Density, g/cm3 8.8
7.9
Embodied Carbon, kg CO2/kg material 3.3
1.5
Embodied Energy, MJ/kg 53
19
Embodied Water, L/kg 370
49

Common Calculations

Stiffness to Weight: Axial, points 7.0
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 8.3
15 to 46
Strength to Weight: Bending, points 10
16 to 34
Thermal Diffusivity, mm2/s 19
12
Thermal Shock Resistance, points 9.5
13 to 38

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.2
0
Carbon (C), % 0
0.090 to 0.15
Chromium (Cr), % 0
0.4 to 0.7
Copper (Cu), % 91 to 94
0 to 0.25
Iron (Fe), % 0 to 0.2
97.2 to 98.7
Lead (Pb), % 0 to 0.3
0
Manganese (Mn), % 0
0.3 to 0.6
Nickel (Ni), % 0 to 0.5
0.5 to 0.8
Phosphorus (P), % 0 to 0.050
0 to 0.025
Silicon (Si), % 0 to 0.0050
0 to 0.3
Sulfur (S), % 0 to 0.050
0 to 0.025
Tin (Sn), % 6.0 to 8.0
0
Zinc (Zn), % 0 to 0.5
0
Residuals, % 0 to 0.6
0