C90200 Bronze vs. Grade C-5 Titanium

C90200 bronze belongs to the copper alloys classification, while grade C-5 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C90200 bronze and the bottom bar is grade C-5 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 70
310
Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 30
6.7
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 41
40
Tensile Strength: Ultimate (UTS), MPa 260
1000
Tensile Strength: Yield (Proof), MPa 110
940

Thermal Properties

Latent Heat of Fusion, J/g 200
410
Maximum Temperature: Mechanical, °C 180
340
Melting Completion (Liquidus), °C 1050
1610
Melting Onset (Solidus), °C 880
1560
Specific Heat Capacity, J/kg-K 370
560
Thermal Conductivity, W/m-K 62
7.1
Thermal Expansion, µm/m-K 18
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 13
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 34
36
Density, g/cm3 8.8
4.4
Embodied Carbon, kg CO2/kg material 3.3
38
Embodied Energy, MJ/kg 53
610
Embodied Water, L/kg 370
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
66
Resilience: Unit (Modulus of Resilience), kJ/m3 55
4200
Stiffness to Weight: Axial, points 7.0
13
Stiffness to Weight: Bending, points 18
35
Strength to Weight: Axial, points 8.3
63
Strength to Weight: Bending, points 10
50
Thermal Diffusivity, mm2/s 19
2.9
Thermal Shock Resistance, points 9.5
71

Alloy Composition

Aluminum (Al), % 0 to 0.0050
5.5 to 6.8
Antimony (Sb), % 0 to 0.2
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 91 to 94
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.2
0 to 0.4
Lead (Pb), % 0 to 0.3
0
Nickel (Ni), % 0 to 0.5
0 to 0.050
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.050
0
Silicon (Si), % 0 to 0.0050
0
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 6.0 to 8.0
0
Titanium (Ti), % 0
87.5 to 91
Vanadium (V), % 0
3.5 to 4.5
Zinc (Zn), % 0 to 0.5
0
Residuals, % 0
0 to 0.4